COATINO®

Preparation

Select the desired amount for the preparation step.

Planned amount

Step 1

Formulation

Pos.	Component	Amount	Producer
1	SILIKOPON® EC	11 g
2	BENTONE® 38	22 g	Elementis
3	1-Methoxy-2-propyl acetate	33 g
4	HEUCODUR® Black 9-100	44 g
5	HEUCOPHOS® ZPO	55 g
6	MICA TM	66 g	Aspanger Bergbau und Mineralwerke GmbH & Co KG
7	AEROSIL® R 972	77 g
8	Butyl glycol acetate	88 g
9	1-Methoxy-2-propyl acetate	99 g
	Total	100.0 g

SILIKOPON® EC

11 g

BENTONE® 38

22 g

Elementis

1-Methoxy-2-propyl acetate

33 g

HEUCODUR® Black 9-100

44 g

HEUCOPHOS® ZPO

55 g

MICA TM

66 g

Aspanger Bergbau und Mineralwerke GmbH & Co KG

AEROSIL® R 972

77 g

Butyl glycol acetate

88 g

1-Methoxy-2-propyl acetate

99 g

Preparation

Weigh in

SILIKOPON® EC

Add components 2 to 7 while stirring.

Dispers in the bead mill until the required particle size is reached (< 20 µm).

Add components 8 to 9 while stirring.

Properties

Attribute	Conditions	Value	unit
Theoretical solids content		approx. 51	%
Cup efflux time	Cup: DIN 4	approx. 30	s
Density		1.29	g/cm³
VOC-Content		approx. 630	g/l

Theoretical solids content

approx. 51 %

Cup efflux time

approx. 30 s

Conditions: Cup: DIN 4

Density

1.29 g/cm³

VOC-Content

approx. 630 g/l

Attribute	Conditions	Value	unit
Flash-off time	23 °C	30	min
Curing condition	250°C	30	min
Wet film thickness		45 - 60	m
Dry film thickness		20 - 25	µm

1K high heat-resistance coating based on SILIKOPON® EC, black

Login

Preparation

Formulation

Preparation

Properties

Formulations variants

Application

Example - High pressure spraying