COATINO®

Preparation

Select the desired amount for the preparation step.

Planned amount

Step 1

Formulation

Pos.	Component	Amount	Producer
1	SILIKOPHEN® AC 900	11 g
2	Xylene	22 g
3	BENTONE® SD-1	33 g	Elementis
4	MICA TM	44 g	Aspanger Bergbau und Mineralwerke GmbH & Co KG
5	HEUCOPHOS® ZPO	55 g
6	HEUCODUR® Black 9-100	66 g
7	AEROSIL® R 972	77 g
8	Plastorit® Super	88 g
9	Butyl glycol acetate	99 g
	Total	100.0 g

SILIKOPHEN® AC 900

11 g

Xylene

22 g

BENTONE® SD-1

33 g

Elementis

MICA TM

44 g

Aspanger Bergbau und Mineralwerke GmbH & Co KG

HEUCOPHOS® ZPO

55 g

HEUCODUR® Black 9-100

66 g

AEROSIL® R 972

77 g

Plastorit® Super

88 g

Butyl glycol acetate

99 g

Preparation

Weigh in

SILIKOPHEN® AC 900

Add components 2 to 8 while stirring.

Dispers in the bead mill until the required particle size is reached (< 20 µm).

Add component 9 while stirring.

Properties

Attribute	Value	unit
Theoretical solids content	approx. 80	%
Density	1.53	g/cm³
VOC-Content	approx. 328	g/l

Theoretical solids content

approx. 80 %

Density

1.53 g/cm³

VOC-Content

approx. 328 g/l

Attribute	Conditions	Value	unit
Dry trough	approx. 23 °C & 50% rH	0.5 - 1	h
Wet film thickness		approx. 100	µm
Dry film thickness		70 - 80	µm

Attribute

Conditions

Value

unit

Dry trough

approx. 23 °C & 50% rH

0.5 - 1

Wet film thickness

approx. 100

µm

Dry film thickness

70 - 80

µm

1K high heat-resistant coating based on SILIKOPHEN® AC 900, black

Login

Preparation

Formulation

Preparation

Properties

Formulations variants

Application

Example - High pressure spraying